Mechanical and tribological behavior of multilayer and monolayer TiN-based coatings

Authors

  • B.K. Kenzhaliyev Institute of Metallurgy and Ore Beneficiation, Kazakhstan
  • A.K. Kenzhegulov Institute of Metallurgy and Ore Beneficiation, Kazakhstan
  • A.A. Mamaeva Institute of Metallurgy and Ore Beneficiation, Kazakhstan
  • A.V. Panichkin Institute of Metallurgy and Ore Beneficiation, Kazakhstan
  • B.B. Kshibekova Institute of Metallurgy and Ore Beneficiation, Kazakhstan

DOI:

https://doi.org/10.51301/ejsu.2025.i3.01

Keywords:

multilayer coating, magnetron sputtering, coefficient of friction, nanohardness, wear resistance

Abstract

This study investigates the mechanical and tribological properties of monolayer TiN coatings and multilayer TiN/TiCN coatings deposited via direct current magnetron sputtering onto titanium substrates (VT1-0). The coatings were characterized by microstructure, nanohardness, elastic modulus, and tribological performance under lubricated friction conditions. Scanning electron microscopy (SEM) revealed that the coatings exhibit a uniform microstructure without visible defects and a typical columnar growth morphology. Nanoindentation tests demonstrated that the multilayer TiN/TiCN coatings possess enhanced hardness (up to 23.5 GPa) and elastic modulus (191 GPa) compared to the monolayer TiN, attributed to interlayer strengthening effects and redistribution of residual stresses. Tribological tests using a ball-on-disk configuration under lubricated conditions showed that the multilayer coatings exhibit a significantly lower coefficient of friction (0.10–0.13) and improved wear resistance compared to the TiN coating. This behavior is associated with TiCN layers, which reduce interfacial adhesion, promote uniform load distribution, and facilitates the formation of a protective tribofilm. The results confirm that the TiN/TiCN multilayer coatings offer superior mechanical and tribological properties, making them promising candidates for engineering components operating under friction and wear conditions.

References

Karar, G.C., Kumar, R. & Chattopadhyaya, S. (2024). De-velopments on friction surfaced coatings for corrosion, wear-resistant and composite. Surface Engineering. 41(1), 8-24. https://doi.org/10.1177/02670844241293139

Abdulvaliev, R.A., Surkova, T.Y., Baltabekova, Z.A., Yessimova, D.M., Stachowicz, M., Smailov, K.M. & Berkinbayeva, A.N. (2025). Effect of amino acids on the ex-traction of copper from sub-conditional raw materials. Kom-pleksnoe Ispolzovanie Mineralnogo Syra = Complex Use of Mineral Resources, 335(4), 50–58. https://doi.org/10.31643/2025/6445.39

Yeligbayeva, G., Khaldun, M., Alfergani, A.A., Tleugali-yeva, Z., Karabayeva, A., Bekbayeva, L., Zhetpisbay, D., Shadin, N. & Atabekova, Z. (2024). Polyurethane as a versa-tile polymer for coating and anti-corrosion applications: A review. Kompleksnoe Ispolzovanie Mineralnogo Syra = Complex Use of Mineral Resources, 331(4), 21–41. https://doi.org/10.31643/2024/6445.36

Shakib, S.E. & Babakhani, A. (2023). Nanomechanical assessment of tribological behavior of TiN/TiCN multi-layer hard coatings deposited by Physical vapor deposition. Jour-nal of Materials Research and Technology, 25, 1344-1354. https://doi.org/10.1016/j.jmrt.2023.05.243

Ospanov, K.K., Smailov, K.M. & Nuruly, Y. (2020). Patterns of non-traditional thermodynamic functions ΔrG⁰/n and Δf(G̅⁰) changes for cobalt minerals. Chemical Bulletin of Ka-zakh National University, 96(1), 22–30. https://doi.org/10.15328/cb1005

Mamayeva, A.A., Kenzhegulov, A.K., Panichkin, A.V., Kshibekova, B.B. & Bakhytuly, N. (2022). Deposition of carbonitride titanium coatings by magnetron sputtering and its effect on tribo-mechanical properties. Kompleksnoe Ispol-zovanie Mineralnogo Syra = Complex Use of Mineral Re-sources, 321(2), 65-78. https://doi.org/10.31643/2022/6445.19

Kenzhegulov, A.K., Mamayeva, A.A. & Panichkin, A.V. (2017). Adhesion properties of calcium phosphate coatings on titanium. Kompleksnoe Ispolzovanie Mineralnogo Syra = Complex Use of Mineral Resources, 3, 35-41.

Bakhytuly, N., Kenzhegulov, A., Nurtanto, M., Aliev, A. & Kuldeev, E. (2023). Microstructure and tribological study of TiAlCN and TiTaCN coatings. Kompleksnoe Ispolzovanie Mineralnogo Syra = Complex Use of Mineral Resources, 327(4), 99-110. https://doi.org/10.31643/2023/6445.45

Su, Y.L. & Kao, W.H. (1998). Tribological behavior and wear mechanisms of TiN/TiCN/TiN multilayer coatings. Journal of Materials Engineering and Performance, 7, 601-612. https://doi.org/10.1361/105994998770347440

Kashyap, A., Harsha, A.P., Barshilia, H.C., Bonu, V., Ku-mar, V.P. & Singh, R. K. (2020). Study of tribological prop-erties of multilayer Ti/TiN coating containing stress-absorbing layers. Journal of Tribology, 142(11), 111401. https://doi.org/10.1115/1.4047195

Galanov, B.A. & Dub, S. (2017). Critical comments to the Oliver–Pharr measurement technique of hardness and elastic modulus by instrumented indentations and refinement of its basic relations. Journal of Superhard Materials, 39(6), 373-389. https://doi.org/10.3103/S1063457617060016

DIN 50324. (1992). Tribology; Testing of friction and wear model test for sliding friction of solids (ball on disc system). German Institute for Standardisation: Berlin, Germany.

Lapitskaya, V.A., Nikolaev, A., Khabarava, A., Sadyrin, E.V., Antipov, P., Abdulvakhidov, K., Aizikovich, S.M. & Chizhik, S. (2023). The influence of nitrogen flow on the stoichiometric composition, structure, mechanical, and mi-crotribological properties of TiN coatings. Materials, 17(1), 120. https://doi.org/10.3390/ma17010120

Zheng, J., Hao, J., Liu, X., Gong, Q. & Liu, W. (2012). A thick TiN/TiCN multilayer film by DC magnetron sputtering. Surface & Coatings Technology, 209, 110-116. https://doi.org/10.1016/j.surfcoat.2012.08.045

Cicek, H. (2018). Wear behaviors of TiN/TiCN/DLC compo-site coatings in different environments. Ceramics Interna-tional, 44(5), 4853-4858. https://doi.org/10.1016/j.ceramint.2017.12.074

Lin, Y.W., Chih, P.C. & Huang, J.H. (2020). Effect of Ti interlayer thickness on mechanical properties and wear re-sistance of TiZrN coatings on AISI D2 steel. Surface and Coatings Technology, 394, 125690. https://doi.org/10.1016/j.surfcoat.2020.125690

Badita-Voicu, L.L., Zapciu, A., Angelescu, D. & Voicu, A.C. (2024). Increasing the wear resistance of hip prostheses components using micro-nanostructured thin layers. Pro-ceedings of the Institution of Mechanical Engineers, Part C: Journal of Mechanical Engineering Science, 09544062241242655 https://doi.org/10.1177/09544062241242655

Musil, J. & Jirout, M. (2007). Toughness of hard nanostruc-tured ceramic thin films. Surface and Coatings Technology, 201, 5148-5152. https://doi.org/10.1016/j.surfcoat.2006.07.020

Leyland, A. & Matthews, A. (2000). On the significance of the H/E ratio in wear control: a nanocomposite coating ap-proach to optimized tribological behavior. Wear, 246, 1-11. https://doi.org/10.1016/S0043-1648(00)00488-9

Leitans, A., Jansons, E., Lungevics, J., Kundzins, K., Boiko, I., Kanders, U. & Linins, O. (2023). Tribological and micro-mechanical properties of the nanostructured carboni-tride/nitride coatings of transition metals alloyed by Hf and Nb. Coatings, 13(3), 552. https://doi.org/10.3390/coatings13030552

Guo, D., Zheng, W.S., Huang, T.L., Zhang, S.L., & Guo, F. (2022). Friction and wear properties of multilayer films de-signed on tantalum substrate. Materials Science Forum, 1078, 121-135. https://doi.org/10.4028/p-l75xgh

Larhlimi, H., Jaghar, N., Lahouij, M., Abegunde, O., Makha, M. & Alami, J. (2024). Effect of carbon content on the tribo-logical behaviour of TiCx coatings prepared by reactive HiP-IMS. International Journal of Refractory Metals and Hard Materials, 120, 106599. https://doi.org/10.1016/j.ijrmhm.2024.106599

Wei, C., Lin, J.F., Jiang, T.H. & Ai, C.F. (2001). Tribological characteristics of titanium nitride and titanium carbonitride multilayer films: Part I. The effect of coating sequence on material and mechanical properties. Thin Solid Films, 381(1), 94-103. https://doi.org/10.1016/S0040-6090(00)01540-6

Madej, M., Kowalczyk, J., Ozimina, D. & Milewski, K. (2018). The tribological properties of titanium carbonitride TiCN coating lubricated with non-toxic cutting fluid. Materi-als Research Proceedings, 5, 47–53. https://doi.org/10.21741/9781945291814-9

Abdulvaliyev, R., Ultarakova, A., Mukangaliyeva, A., Lokhova, N. & Kassymzhanov, K. (2024). Comparative analysis of acid leaching for the efficient recovery of lan-thanum and cerium from phosphate. Separations, 11, 288. https://doi.org/10.3390/separations11100288

Zhang, P., Ying, P., Lin, C., Yang, T., Wu, J., Huang, M., ... & Levchenko, V. (2021). Effect of modulation periods on the mechanical and tribological performance of MoS₂–TiL/MoS₂–TiH multilayer coatings. Coatings, 11(10), 1230. https://doi.org/10.3390/coatings11101230

Downloads

Published

2025-06-30

How to Cite

Kenzhaliyev, B. ., Kenzhegulov, A. ., Mamaeva, A. ., Panichkin, A. ., & Kshibekova, B. . (2025). Mechanical and tribological behavior of multilayer and monolayer TiN-based coatings. Engineering Journal of Satbayev University, 147(3), 1–6. https://doi.org/10.51301/ejsu.2025.i3.01

Issue

Vol. 147 No. 3 (2025): Engineering Journal of Satbayev University

Section

Metallurgy

License

Copyright (c) 2025 Engineering Journal of Satbayev University

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

<div class="pkpfooter-son">
<a rel="license" href="http://creativecommons.org/licenses/by-nc/4.0/"><img alt="Creative Commons License" style="border-width:0" src="https://i.creativecommons.org/l/by-nc/4.0/80x15.png"></a><br>This work is licensed under a <a rel="license" href="http://creativecommons.org/licenses/by-nc/4.0/">Creative Commons Attribution-NonCommercial 4.0 International License</a>.
</div>